Is glue the answer to climate change?

They have developed a new material capable of capturing the greenhouse gas carbon dioxide (CO₂) with the key ingredient being a common epoxy resin you probably have at home.

Carbon capture materials are a crucial part of a range of technologies, alongside renewables and energy efficiency solutions, that can help reduce the amount of CO₂we release into the atmosphere.

“我们通常表明小分子环氧但书d in glues can stick larger ones together to make effective carbon capture materials potentially useful to tackle climate change," said Dr Enrico Andreoli, lead of the research study now subject of a paper published inChemistry of Materials.

Dr Louise Hamdy, first author of the paper, added "We've developed a new approach to making an effective CO₂capture material from a widely studied CO₂-reactive polyamine by reaction with an industrially mass-produced epoxy resin. This material shows very high CO₂uptake and could potentially be used to capture CO₂from industrial flue gas streams or from the air, relieving us from some of the worst effects of global warming."

Current CO₂capture technologies need to be significantly advanced. Major challenges include materials cost, capacity, CO₂-selectivity, regeneration, robustness and stability to water. Solid CO₂capture materials composed of polyamines supported on alumina or silica have emerged as promising carbon capture materials.

However, rather than follow suit, the researchers at ESRI cross-linked the polyamine into a solid by using epoxy resin -- constituting just one-tenth of the mass of the material -- maximising the CO₂-reactive component and avoiding the use of a support. "This confirms the validity of my original idea of using cross-linking as an alternative to bulky supports," said Andreoli.

The cross-linked material modified with a hydrophobic additive captured almost 20% of its weight in pure CO₂at 90 °C. This finding confirmed a previous hypothesis that the introduction hydrophobic groups can disrupt the internal structure of the material to promote CO₂uptake by the polyamine.

The additive not only increased the amount of captured CO₂but did so at a lower temperature. Hamdy commented, "This finding is significant as it proves that through the introduction of additives, we can fine tune these materials for optimum performance at specific working temperatures."

Experiments revealed the functionalised sample to be highly selective for CO₂在氮(N2),显示N的吸收可以忽略不计2. Selectivity was further explored by testing the material performance under flue gas-like conditions. This revealed that the sample could capture 9.5% of its weight in CO₂under a dilute CO₂stream of 10% CO₂/90% N2 at 90 °C in only 15 minutes.

On subjecting the material to repetitive capture cycles, increasing the temperature to 155 °C under pure CO₂for 5 minutes to regenerate, the material showed no loss of capacity for 29 cycles, testament to the robustness of the material.

The functionalised material also performed exceptionally well under humid conditions -- often a huge challenge for many CO₂sorbent solids. At 25 °C, in pure CO₂, the pre-hydrated material was able to capture an impressive 23.5%. This opens up the possibility of this material being developed for capture of CO₂directly from the air.

"This research is defining a new and promising direction to economical and effective carbon capture materials. Our institute has a strong focus on developing and deploying new technologies in the field of carbon capture, utilisation, and storage. This paper is evidence of the level of our expertise," said Professor Andrew Barron, founder and director of ESRI.